【参考】JIS与GB材料性能对照表(2)


GB(CHINA) and JIS(JAPAN) material comparison for XUSN6 project(TOSHIBA)
GB/T 1222-1984 55Si2Mn
Std JIS Chemical composition C Si Mn P 700-88 Q0SWOSM-B 0.52~0.60 1.50~2.00 0.60~0.90 ≤0.035 Tensile requirement Yield strength(N/mm2) Tensile strength(N/mm2) Std.No Designation 1176 1274 S ≤0.035 Cr ≤0.35 Ni ≤0.35 Cu ≤0.25

GB/T 3077-1988 35CrMo
Chemical composition C Si Mn P JIS 700-88 SCM435-Q 0.32~0.40 0.17~0.37 0.40~0.70 ≤0.035 Tensile requirement Yield strength(N/mm2) Tensile Thickness(mm) strength(N/mm2) ≤16 >16~40 >40~60 >60~100 >100~150 >150 235 225 215 205 195 185 375~500 Std Std.No Designation S Cr Mo ≤0.035 0.80~1.10 0.15~0.25 Impact Examination "V"type Temp:-20°C ≥7 Cu ≤0.20

JIS G5101 SC450
Std GB Std.No Designation C Si ≤0.3 ≤0.5 Tensile requirement Chemical composition Mn P 0.9 ≤0.05 Tensile strength(N/mm2) ≥450 S ≤0.04

11352-89 ZG230~450

Yield strength(N/mm2) ≥230

JIS G4202 SACM645
Std GB/T Std GB/T Std.No 3077-88 Std.No 3077-88 Designation 38CrMoAlA Designation 35CrMoA C 0.35~0.42 Chemical composition Si Mn P 0.20~0.45 0.30~0.60 ≤0.025 Chemical composition Si Mn P 0.17~0.37 0.40~0.70 ≤0.025 S ≤0.025 Cr Mo 1.35~1.65 0.15~0.25 Ni ≤0.3 AL others 0.7~1.10 Cu≤0.25

JIS G4202 SCM435
C 0.32~0.40 S ≤0.025 Cr 0.8~1.0 Mo 0.15~0.25 Ni ≤0.3 others Cu≤0.25

第1页 共3页

GB(CHINA) and JIS(JAPAN) material comparison for XUSN6 project(TOSHIBA)
JIS G4051 S25C
Std GB/T Std.No 699-88 Designation C 25 0.22~0.30 Chemical composition Si Mn P 0.17~0.37 0.50~0.80 ≤0.035 S ≤0.035 Cr ≤0.25 Ni ≤0.25 others Cu≤0.25

JIS G4051 S45C
Std GB/T Std.No 699-88 Designation C 45 0.42~0.50 Chemical composition Si Mn P 0.17~0.37 0.50~0.80 ≤0.035 S ≤0.035 Cr ≤0.25 Ni ≤0.25 others Cu≤0.25

JIS G3456 STPT370
Std GB/T Std.No 699-88 Designation Chemical composition C Si Mn P S 20 0.17~0.24 0.17~0.37 0.35~0.65 ≤0.035 ≤0.035 Tensile requirement Tensile Yield strength(N/mm2) strength(N/mm2) ≥245 ≥410 Chemical composition Mn P 0.50~0.80 ≤0.035 Tensile strength(N/mm2) ≥1080 Cr ≤0.25 Ni ≤0.25 others Cu≤0.25

K5P51B(TOSHIBA STANDARD)1
Std GB/T Std.No Designation C Si 0.38~0.45 0.17~0.37 Tensile requirement S ≤0.035 Cr 0.90~1.20 V Ni Mo others 0.15~0.30

3077 42CrMo

Yield strength(N/mm2) ≥930

K5P51B(TOSHIBA STANDARD)2
Std GB/T Std.No 3077-88 Chemical composition C Si Mn P S 42CrMo 0.38~0.45 0.17~0.37 0.50~0.80 ≤0.035 ≤0.035 Tensile requirement Tensile Yield strength(N/mm2) strength(N/mm2) ≥930 ≥1080 Designation Cr 0.9~1.20 Ni Mo others 0.15~0.30

第2页 共3页

GB(CHINA) and JIS(JAPAN) material comparison for XUSN6 project(TOSHIBA)
JIS G 4309 SUS304-SW / SUS304-W1
Std GB/T Std.No Designation C Si ≤0.08 ≤1.00 Tensile requirement Chemical composition Mn P ≤2.50 ≤0.035 Tensile strength(N/mm2) ≥550 Chemical composition Mn P S ≤0.030 Cr 18.00~20.00 Ni 7.00~10.50 others Cu≤0.25

3280 0Cr19Ni9

Yield strength(N/mm2) ≥275

JIS G 5501 FC250
Std GB/T Std.No Designation C Si S Cr Ni others

9439 HT250 Tensile requirement Tensile strength(N/mm2) Thickness(mm) 10~20 20~30 240 220

4.0~10 270

30~50 200

JIS H3250 C3603
Std GB/T Std.No Designation Cu 58.0~63.0 Pb 0.5~2.5 Chemical composition Zn Al balance 0.2~0.8 Elongation % 15~20 Tensile strength(N/mm2) 220~280

1176-1987 ZHPb59-1

Hardness (HB) 80.07~90.27

ASTM A234-WPB
Std GB/T Std.No 699-88 Designation C 25 0.22~0.30 Chemical composition Si Mn P 0.17~0.37 0.50~0.80 ≤0.035 S ≤0.035 Cr ≤0.25 Ni ≤0.25 others Cu≤0.25

第3页 共3页


赞助商链接
相关文章:
40Cr特性大全
JIS G4053 ASTM A29/ ISO 683-18:1996 二 化学...≤207 四 40cr 介绍 【参考对应钢号】我国 GB 的...节约材料又减少机械加工的工作量,还 可改善机械性能...
GBASTMJISDIN标准各种材质不锈钢的化学成分一览表
GBASTMJISDIN标准各种材质不锈钢的化学成分一览表_材料科学_工程科技_专业资料。...GB ASTM 1Cr19Ni9 TP304H 0.040.10 0.040.10 《1.00 《1.00 《2....
各国材料对照表
Mo2 日本 JIS SMn420 SMn433 SMn438 SMn443 SCr...材料对照表注:表中括号内分别为 GB 标准,JIS 标准...各国标准对照表参考资料 1页 1下载券 材料对照表...
常用材料牌号对照表
常用材料牌号对照表_材料科学_工程科技_专业资料。常用材料牌号对照表 种类 GB ...[84] JIS GB3220-92[84] 美国 AISI UNS BS 970 Part4 BS 1449 Part2 ...
部分紧固件国家标准与国际标准对照表
JIS B 1189: 2005 DIN EN ISO 4016 DIN EN ISO 4018 DIN EN ISO 4014 ...性能等级 5、 8 ISO 7040:1997 10 级 7 8 9 10 GB/T 889.2-2000...
JIS_Z2241-2-1998 金属材料拉伸试验方法
国家标准 金属材料拉伸试验方法 JIS Z 2241 内部资料 仅供参考 如有疑问 以...2. 1)上屈服强度【upper yi el d st r ess(ReH) 】 试样发生屈服而力...
原材料化学成份,机械性能表
JIS 机械性能 σb≥200 GB12226-200 5 德 DIN ...J/cm2 棒材化学成份、机械性能表材料牌号 410 1Cr... Mn 为主要元素 机械性能 化学成份 机械性能 ...
主要国家气门材料对照表(参考件)
2.20~3.00 Cr 8.00~10.00 序号 元素 根据表 1 而制定的治炼分析范围...【参考】JIS与GB材料性能... 3页 免费 国家清洁生产项目资金申... 39页 ...
中国、日本和美国金属材料室温拉伸试验标准对比
拉伸试验标准对比拉伸试验是材料力学性能测试中最常见...因为 GB 标准 JIS 标准只使用公制单 位,所以...2. 试验机及其附属设备 2.1 引伸计 表 1. E ...
各国常用材料对照表
(蒙耐尔) 中日部分黑色金属材料对照表(参考) molds...国家和标准 加工特性材料编号 1 1.040 1 1.0...GB BS EN AFNO R UNI NBN SS UN E JIS AISI...
更多相关标签: