Chemical Composition (%) Copper Alloy No. CuSn3Zn8Pb6Ni1 CuSn3Zn11Pb4 CuSn5Pb5Zn5 CuSn10Pb1 CuSn10Zn2 ASTM No. C83800 C84500 C83600 C90700 C90500 Sn 2.0~4.0 2.0~4.0 4.0~6.0 9.0~11.5 9.0~11.0 Zn Pb P ---0.5~1.0 -Ni 0.5~1.5 1.0 1.0 0.10 1.0 Cu Bal Bal Bal Bal Bal

6.0~9.0 4.0~7.0 9.0~13.0 3.0~6.0 4.0~6.0 4.0~6.0 -1.0~3.0 ---

Cast Tin Bronze Chemical Composition & Mechanical Property Mechanical Property, ≥ Copper Alloy No. Casting Process Tensile Strength Yield Strength Elongation σb/MPa σ0.2/MPa δ5 (%) (kgf/mm2) (kgf/mm2) 175(17.8) 215(21.9) 175(17.8) 215(21.9) 200(20.4) 200(20.4) 250(25.5) 250(25.5) 220(22.4) 310(31.6) 330(33.6) 360(36.7) 240(24.5) 245(25.0) 270(27.5) 270(27.5) ----90(9.2) 90(9.2) 100(10.2) 100(10.2) 130(13.3) 170(17.3) 170(17.3) 170(17.3) 120(12.1) 140(14.30 140(14.3) 140(14.3) 8 10 8 10 13 13 13 13 3 2 4 6 12 6 7 7 Brinell Hardness (HBS) 590 685 590 590 590 590 635 635 785 885 885 885 685 785 785 785

CuSn3Zn8Pb6Ni1 Sand Mould Casting C83800 Metal Mould Casting CuSn3Zn11Pb4 C84500 CuSn5Pb5Zn5 C83600 Sand Mould Casting Metal Mould Casting Sand Mould Casting Metal Mould Casting Centrifugal Casting Continuous Casting Sand Mould Casting Metal Mould Casting Centrifugal Casting Continuous Casting Sand Mould Casting Metal Mould Casting Centrifugal Casting Continuous Casting

CuSn10Pb1 C90700

CuSn10Zn2 C90500

Cast Aluminum Bronze Chemical Composition & Mechanical Property Copper Alloy No. CuAl8Mn13Fe3Ni2 CuAl9Fe4Ni4Mn2 CuAl10Fe3 ASTM No. Ni C95700 C95800 C95200 1.8~2.5 Chemical Composition (%) Al 7.0~8.5 Fe Mn Cu Bal Bal Bal

2.5~4.0 11.5~14.0

4.0~5.0 8.5~10.0 4.0~5.0 0.8~2.5 8.5~11.0 2.0~4.0

Mechanical Property, ≥ Brinell Tensile Strength Yield Strength Elongation Hardness σb/MPa σ0.2/MPa δ5 (%) (kgf/mm2) (kgf/mm2) (HBS) 645(65.8) 280(28.6) 20 1570 CuAl8Mn13Fe3Ni2 Sand Mould Casting C95700 Metal Mould Casting 670(68.3) 310(31.6) 18 1665 CuAl9Fe4Ni4Mn2 Sand Mould Casting 630(64.3) 250(25.5) 16 1570 C95800 490(50.0) 180(18.4) 13 980 Sand Mould Casting Metal Mould Casting 540(55.1) 200(20.4) 15 1080 CuAl10Fe3 C95200 Centrifugal Casting 540(55.1) 200(20.4) 15 1080 Continuous Casting 540(55.1) 200(20.4) 15 1080 Copper Alloy No. Casting Process

Cast Brass Chemical Composition & Mechanical property Copper Alloy No. ASTM No. C28000 CuZn38 CuZn25Al6Fe3Mn3 C85500 C86300 Zn Bal Bal Bal Chemical Composition (%) Pb Al Fe Mn 0.30 ---0.07 -Cu 59.0~63.0

---60.0~63.0 4.5~7.0 2.0~4.0 1.5~4.0 60.0~66.0

CuZn26Al4Fe3Mn3 CuZn35Al2Mn2Fe1 CuZn40Mn3Fe1 CuZn33Pb2 CuZn40Pb2

C86200 C86500 C86800 C85400 C85700

Bal -- 2.5~5.0 1.5~4.0 1.5~4.0 60.0~66.0 Bal -- 0.5~2.5 0.5~2.0 0.1~3.0 57.0~65.0 Bal --- 0.5~1.5 3.0~4.0 53.0~58.0 Bal 1.0~3.0 ---63.0~67.0 Bal 0.5~2.5 0.2~0.8 --58.0~63.0

Copper Alloy No. C28000 CuZn38 C85500 CuZn25Al6Fe3Mn3 C86300 CuZn26Al4Fe3Mn3 C86200 CuZn35Al2Mn2Fe1 C86500 CuZn40Mn3Fe1 C86800 CuZn33Pb2

铸造方法

Mechanical property, ≥ σb/MPa(kgf/mm )
2

σ0.2/MPa(kgf/mm )

2

δ5(%)

硬度 HBW

S J S J Li、La S J Li、La S J Li、La S J

295(30.0) 295(30.0) 725(73.9) 740(75.5) 740(75.5) 600(61.2) 600(61.2) 600(61.2) 450(45.9) 475(48.4) 475(48.4) 440(44.9) 490(50.0) 380(38.7) 400(40.8) 400(40.8) 300(30.6) 300(30.6) 300(30.6) 170(17.3) 200(20.4) 200(20.4)

30 30 10 7 7 18 18 18 20 18 18 18 15

590 685 1570 1665 1665 1175 1275 1275 980 1080 1080 980 1080

S C85400 CuZn40Pb2 C85700 S J

180(18.4)

70(7.1)

12

490

220(22.4) 280(28.6) 120(12.2)

15 20

785 885



相关文章:
常用铜合金材料分类及特性_图文
含锌低於 36%的黄铜合金由固溶 体组成﹐具有良好的冷加工性能﹐如含锌 30%...铜及铜合金牌号对照表 CONVERSION TABLE OF GRADES FOR COPPER & ITS ALLOYS ...
铜合金的牌号和应用
铜合金的牌号和应用_材料科学_工程科技_专业资料。根据黄铜中所含合金元素种类的...性能良,切削性优 HPb59-1 冷热加工性能均优,切削性良 铅黄铜国标可见下表: ...
铜合金的显微组织和力学性能.doc赵菲
铜合金的显微组织和力学性能.doc赵菲_工程科技_专业资料。铜合金的显微组织和力学...Zr 合金室温和高温 3.2 力学性能 拉伸试验在室温和高温进行的结果表 2 所示...
铜及铜合金系列
主要性能指标: 钴 Co 0.35-0.65 镍 Ni 0.20-0.25 铜 Cu 余量 硅 Si <0.15 铁 Fe <0.15 铝 Al <0.15 名比 称重(g/cm ) 3 高强度铍铜合金 ...
铜及其合金的分类和性能
铜及其合金的分类和性能 - 铜及其合金的分类和性能 铜及铜合金具有优良的导电性能、导热性能、抗腐蚀性能和良好的成形性能,在 电气、化工、机械、动力、交通等工业...
铜牌号及标准
各国铜牌号及标准对照表中国 GB KRUZZEICHEN TU2 T2 TP2 TP1 H96 H90 H85 ...C7701 C7521 C7060 C7150 第二节 铜及铜合金 铜及铜合金具有以下性能特点。...
铜及铜合金概述
铜及铜合金概述_专业资料。铜及铜合金概述 铜是人类最早发现和使用的金属材料,铜的熔点低,易合金化,是人类使用的最古老的 金属之一,早在公元前 7000 年人类就...
铜的分类以及性能
无气孔、沙眼、疏松,导电性能极佳,电蚀出的 模具表面 铜合金精度高,经热处理工艺,电极无方向性,适合精打,细打,性能与日本纯红 铜相当,价格更实惠,是替代进口...
铜及铜合金特性与用途
2页 1财富值 各种铜合金的特性表 1页 1财富值喜欢此文档的还喜欢 ...锡磷青铜是一种合金铜,具有良好的导 电性能,不易发热、确保安全同时具备很强...
C22000铜合金应用研究
C22000铜合金应用研究 - 性能和H96相似,但强度较H96稍高,有良好的力学性能和压力加工性能,表面处理性能好,可镀金属及涂敷珐琅。
更多相关标签: